Agsar Port City High Gloss Enamel Paint is a modern synthetic enamel paint, economically priced. It gives a high gloss and can withstand extreme climatic condition. Agsar Port City synthetic Enamel can be used for painting doors, windows, furniture, electric motors, fans, walls etc. Agsar High Gloss Enamel can be used for writing signboards, wall advertisements etc. As the finish and gloss withstand severe exterior conditions of wind, sun, rain and cold.
| 1. | Viscosity of supply | 110-120 seconds by Ford cup No.B4 at 30° C |
| 2. | Shades available | As per shade card |
| 3. | Packs available | 20,4,1 lit and 500,200,100,50 ml in selected popular shades |
| 4. | Surface to be painted | Metals, woods, plaster and a number of other surfaces |
| 5. | Primer to be used |
Ferrous surfaces: Agsar Red Oxide Metal Primer Aluminium or Galvanised steel: Agsar Zinc Chrome Metal Primer Wood: Agsar Wood Primer –White/Pink Plaster: Agsar Cement Primer Oil Base Other surfaces: Depending on the surface |
| 6. | Method of application | Brush, Roller and spray |
| 7. | Viscosity of application | Brushing and rolling 60-65 secs by Ford Cup No.B4; Spraying 30-40 secs by B4 at a pressure of 3.5 Kg per cm2 |
| 8. | Thinner to be used | General purpose thinner |
| 9 | Drying time | Surface drying within 3 hours, hard drying within 18 hours. The above varies with atmospheric temperature and humidity |
| 10. | Average coverage capacity per coat | 135-200 square feet per litre per coat depending upon the shade and surface. |
| 11. | Finish | Mirror like gloss |
| 12. | General Directions for use | The surface to be painted should be dry and free from dirt, grease, oil and loose matter. Prime the surfaces with the recommended primer. Use of Agsar Knifing paste filler is recommended if necessary to fillup the dents and surface imperfections. Then sand the surface with emery paper and apply one more coat of primer before applying the enamel. Do not apply too thick a coat. Allow the paint to dry for 10-12 hours before applying the second coat. |